What is the yield strength of aluminum?
Aluminum 6061-T6; 6061-T651
| Physical Properties | Metric | English |
|---|---|---|
| Hardness, Rockwell B | 60 | 60 |
| Hardness, Vickers | 107 | 107 |
| Ultimate Tensile Strength | 310 MPa | 45000 psi |
| Tensile Yield Strength | 276 MPa | 40000 psi |
What is the difference between 6061 and 6082 aluminium?
As a relatively new alloy, the higher strength of 6082 has seen it replace 6061 in many applications. The addition of a large amount of manganese controls the grain structure which in turn results in a stronger alloy. It is difficult to produce thin walled, complicated extrusion shapes in alloy 6082.
What is the difference between 6061 t6 and 6082 t6?
6061 and 6082 aluminum alloy are the alloy in the aluminum-magnesium-silicon family (6xxx series). The main difference is that the composition ratios of silicon and magnesium in 6082 and 6061 are different.
What is the yield strength of 6061 aluminum?
6061-T6. T6 temper 6061 has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa).
Which is stronger aluminium or Aluminium alloy?
No, there is no difference between the Aluminium and Aluminum. As far as the element is concerned, there is no difference. The only thing that makes these two words distinct is how they are spelled.
What is the stock availability of aluminium alloy 6082?
Aluminum Alloy 6082 is available in Sheet and Plate (typical stock availabillity) , Aluminum 6082 Bar, 6082 is also available in Drawn Tube, Tube and Forging Stock. For all stock availability of Aluminium Alloy 6082 contact Sales. Aluminium alloy 6082 also corresponds to the following standard designations and specification.
What is the strength of 6082?
Alloy 6082 is a medium strength alloy with excellent corrosion resistance. Alloy 6082 has the highest strength of the 6000 series alloy.
What are the different tempers for 6082 aluminium?
The most common tempers for 6082 aluminium are: Solution heat treated and naturally aged to a substantially stable condition Solution heat treated, stress relieved by stretching then artificially aged.
What is the difference between 6082 and T651 alloys?
The extruded surface finish is not as smooth as other similar strength alloys in the 6000 series. In the T6 and T651 temper, 6082 machines well and produces tight coils of swarf when chip breakers are used.